BCMaterials Fortnightly Seminar #49: Ariane Sagasti and Andrés Martin
ARIANE SAGASTI
(BCMATERIALS)
MAGNETOELASTIC RESONATOR FOR HIGHLY SPECIFIC CHEMICAL AND BIOLOGICAL DETECTION: A CRITICAL STUDY
We have developed a detection system made of an amorphous ferromagnetic ribbon of composition Fe64Co17Si6.6B12.4, with excellent magnetoelastic properties as saturation magnetostriction of 23 ppm and DE effect of 27%. The resonators were coated with polystyrene (PS). Consecutive depositions were applied by dip coating from 10 to 100 µM solution in tetrahydrofuran (THF). The mass increment after each deposition was accurately measured with a high precision (0,1µg) balance, and compared with the corresponding resonant frequency. We have tested resonators with L=3, 2 and 1 cm length. As theory predicts, we have observed a decrease on that resonant frequency as the PS mass increases, reaching a maximum sensitivity of S=Df/Dm=54,9 Hz/µg (that corresponds to 18 ng detection for 1 Hz resolution), for the 1 cm length resonator. Nevertheless, our measurements show even better results than theoretically predicted by the common resonator model. Bearing this in mind, here we present a critical study on the conditions for an optimum performance of such resonance-based sensing devices, both from the point of view of the magnetoelastic resonance conditions and from the layer deposition procedure.
ANDRES MARTIN
(BCMATERIALS)
TETRAGONAL CE-BASED CE-SM(FE,CO,TI)12 ALLOYS FOR PERMANENT MAGNETS
Rare-earth intermetallic compounds with composition R(Fe,Co)12 crystallize into a tetragonal structure of the type ThMn12 with uniaxial anisotropy. This structure is stabilized with the addition of a non-magnetic element (Mo,Ti,V...) that leads to lower values of magnetization. Among these materials the Ce-based compounds have been very attractive recently because of the low cost of Ce which is much more abundant than the other rare earths. In this work, we have studied the magnetic and structural properties of Sm1-xCexFe9Co2Ti ribbons (x=1, 0.75, 0.5, 0.25) melt-spun with wheel speed of 15 m/s and 35 m/s. The melt-spun samples were annealed at temperatures in the 700-800 oC range to obtain the desired 1:12 tetragonal phase with optimum hard magnetic properties. The Sm-free CeFe9Co2Ti samples spun at 35 m/s showed a negligible coercivity suggesting that they are amorphous while the ones spun at 15 m/s show a smooth hysteresis loop with a coercivity of 540 Oe. On the other hand, the Ce.5Sm.5Fe9Co2Ti samples spun at wheel speed 15 m/s show a smooth hysteresis loop with a coercivity of 1404 Oe as compared to the samples spun at higher speeds which show a constricted loop suggesting a decoupled mixture of soft and hard phases, which were identified by x-ray diffraction as bcc-Fe and 1:12 tetragonal phases, respectively. Annealing at 700 oC was found to increase the coercivity substantially with maximum values of 778 Oe for the former and 2010 Oe for the latter compositions.
Related news
BCMaterials coorganiza la 44º reunión del Grupo de Electroquímica de la RSEQ en Leioa
BCMaterials, en colaboración con la Facultad de Ciencia y Tecnología de la UPV/EHU, organiza la 44ª Reunión del Grupo Especializado de Electroquímica de la Real Sociedad Española de Química (RSEQ)....Nueva portada en ACS Biomaterials Science & Engineering
La publicación realizada por BCMaterials y colaboradores “Cryo-Electrohydrodynamic Jetting of Aqueous Silk Fibroin Solutions”, ha sido seleccionada como portada de la revista ACS Biomaterials...Número especial: ‘Chemistry in Ukraine’
The Chemical Record, revista de la Sociedad Química de Japón, ha publicado el número especial 'Chemistry in Ukraine', coordinado por el Ikerbasque Research Professor Stefan Wuttke en colaboración con...Charla invitada de Santiago Rodríguez el 26 de marzo
BCMaterials ofrecerá una nueva charla invitada el próximo 26 de marzo, con Santiago Rodríguez Jiménez, investigador postdoctoral del Departamento de Química de la Universidad de Cambridge (Reino...